For wet lay-up: ideal for bonding and impregnating composite fabrics.
Biobased: contains 34% renewable materials, reducing the impact on the environment.
Mechanical properties: maintains excellent performance under mechanical and thermal stress.
Suitable viscosity: low viscosity for fast, effective fibre impregnation.
Enhanced durability: excellent resistance to moist heat, ideal for demanding environments.
Pro-SET LAM-125G biobased epoxy resin is specially formulated to meet the needs of wet lamination, offering a durable, high-performance solution for the manufacture of lightweight composite materials.
With a 34% biobased content, this resin is a more environmentally friendly manufacturing solution.
Its low viscosity enables rapid and complete impregnation of composite fibres, including Kevlar® and carbon fibres, which is crucial for applications requiring impeccable clarity and surface finish.
LAM-125G is also designed to allow extended working times, facilitating the lamination process in a variety of conditions.
It provides excellent thermal and mechanical properties, curing at room temperature and requiring post-cure to achieve maximum properties.
The resin is ideal for a variety of applications, including the manufacture of demanding, high-performance structural components in the marine, automotive and aerospace sectors.
Technical specifications LAM-125G/LAM-224
Pot life 150g: 13 minutes at 25°C
Mixed viscosity: 616 mPas at 25°C
Type D hardness: 87
Compressive strength: 112 MPa
Tensile strength: 79 MPa
Flexural strength: 126 MPa
Ultimate Tg: 89°C
Technical data LAM-125G/LAM-226
Pot life 150g: 59 minutes at 25°C
Mixed viscosity: 475 mPas at 25°C
Type D hardness: 86
Compressive strength: 111 MPa
Tensile strength: 53 MPa
Flexural strength: 90 MPa
Ultimate Tg: 91°C
Technical data LAM-125G/LAM-229
Pot life 150g: 100 minutes at 25°C
Mixed viscosity: 449 cP at 25°C
Type D hardness: 86
Compressive strength: 108 MPa
Tensile strength: 51 MPa
Flexural strength: 89 MPa
Ultimate Tg: 89°C