KIT 305 1.38S. Biobased epoxy resin 305 for compression molding processes 1kg + slow hardener CPS 0.38kg
Biobased epoxy resin for compression molding processes for fast cycling
Rapid heat activated polymerization for high temperature compression molding processes.
Common uses: Skis and Snowboards, Skateboards, Compression molding composites, Wood laminates.
Super Sap® formulation.
28% biobased content
USDA BioPreferred® certified
Resin 305 is a compression molding resin for rapid cycling in heat-assisted molding processes of fiber reinforced composites.
The 305 system has a high organic content, excellent fiber impregnation qualities and thixotropic characteristics to limit sagging in high temperature curing applications.
High modulus combined with excellent elongation properties results in durable yet lightweight composite parts.
305 epoxy resin is a USDA BioPreferred product with a 28% biobased content
Usage : skateboard, skis, snowboards, press molding composites
Consumption: about 3 liters for 2 snowboards or 2 pairs of skis
Usage advice:
-For best results, make the mixing ratio of the two components according to the weights
-Always mix the product thoroughly for at least 2 minutes, scraping all surfaces of the container to ensure even mixing
-Use the product in an environment with cold ambient temperatures or high humidity
-For optimum curing performance, make sure surfaces are dry and free of dirt, debris and/or oil. Surface preparation by sanding is strongly recommended
-Conduct pre-testing with the materials and processes being considered to fully understand the curing characteristics of the epoxy in your working environment with the materials.
Available options:
- 305 CPM resin + CPF fast curing agent
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:40
Mixing viscosity (cPs) at 25°C : 1994
Pot life at 25°C : 20 minutes
Recommended full cure: 15 minutes at 82°C
Characteristics : superior adhesion, very low viscosity to facilitate the wetting of the fibers and accelerate the polymerization for high production rates.
- 305 CPM resin + CPS fast hardener
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:38
Mixing viscosity (cPs) at 25°C : 1546
Pot life at 25°C: 50 minutes
Recommended full cure: 20 minutes at 82°C
Characteristics: Superior adhesion, very low viscosity to facilitate fiber wetting.