KIT ONE 14.3F. ONE 10kg low viscosity biobased laminating resin + ONF 4.3kg fast hardener
Biobased epoxy resin with high content of bio-components for lamination, composite applications, coating and adhesives
Fast curing, low viscosity and fast air release property.
Common uses: Fiberglass composites, natural fiber composites, woodworking, epoxy coatings, fiberglass boat repair, adhesives and sealants, surfboards, Stand Up Paddle Boards and Handplanes
Super Sap® formulation.
30% biobased content
USDA BioPreferred Certified
ONE is a general purpose laminating resin with a high biobase content for laminating, coating and bonding applications of composites.
This system features faster speed, low viscosity, fast debubbling, ideal for fibre reinforced composite lamination and coating.
ONE is a USDA-certified BioPreferred® product with a 30% biobase content.
Usage: wood, coating, marine application, gluing
Consumption: a 6L kit = 32.5m². Consumption is reduced by 50% on porous substrates or fibre reinforcement.
Working temperature : optimal temperature from 21°C to 30°C.
Environment :
- BIO-REFINERY: Traditional raw materials based on petroleum carbon are replaced by materials based on renewable vegetal carbon or co-produced by other industrial processes.
- RESIN FORMULATION: Green chemistry techniques ensure energy-efficient formulation and fewer harmful by-products.
- SUPER SAP: technology that saves energy, minimises harmful by-products and reduces greenhouse gas emissions.
Application tips :
- For best results, measure both components by weight to within 5% of the recommended mixing ratio.
- Always mix the product for at least two minutes, scraping the container to ensure thorough mixing.
- Use products in a controlled environment; avoid high humidity and low temperatures.
- Animes, a by-product of the curing process, appear as a waxy film on the cured epoxy and are more visible in cool, damp conditions. It can clog the sandpaper and inhibit adhesion.
- The amine is soluble in water and is easily removed with clean water (no solvent) and an abrasive pad.
- For good adhesion, epoxy bonding surfaces must be clean, dry and sanded.
- If you are unfamiliar with the product, create small test samples before starting a larger scale project.
Available options :
Resin ONE + fast hardener ONF
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:43
Mixing viscosity (cPs at 25°C): 1020
Time of use (at 25°C): 18 minutes
Dry to the touch (at 25°C): 3 hours
Recommended complete curing: 7 days at 25°C
Characteristics: slightly amber colour
Applications: general laminating work, gluing, coating, manual layering of layers
Resin ONE + slow hardener ONS
Mixing ratio by volume: 2:1
Mixing ratio by weight: 100:43
Mixing viscosity (cPs at 25°C): 1020
Time of use (at 25°C): 43 minutes
Dry to the touch (at 25°C): 8 hours
Recommended full cure: 7 days at 25°C (post cure recommended)
Characteristics: slightly amber colour
Applications: general laminating work, gluing, coating, manual layering of layers