Reference:
ER-ONE-2

ONE ENTROPY biobased resin for lamination. Low viscosity. For general use (2kg)

Biobased epoxy resin with high content of bio-components for lamination, composite applications, coating and adhesives

Fast curing, low viscosity and fast air release property.

Common uses: Fiberglass composites, natural fiber composites, woodworking, epoxy coatings, fiberglass boat repair, adhesives and sealants, surfboards, Stand Up Paddle Boards and Handplanes

Combine with ONS slow hardeners and ONF fast hardeners

Super Sap® formulation.

30% biobased content

USDA BioPreferred certified

Read more
€74.16 (VAT incl.)
In stock 4 Items

   

Description

ONE is a general purpose biobased laminating resin with high bio-component content for composite lamination, coating and bonding applications.

This system features faster speed, low viscosity, fast debubbling, ideal for fibre reinforced composite lamination and coating.

ONE is a USDA-certified BioPreferred® product with a 30% biobase content.

Usage: wood, coating, marine application, gluing

Consumption: a 6L kit = 32.5m². Consumption is reduced by 50% on porous substrates or fibre reinforcement.

Working temperature : optimal temperature from 21°C to 30°C.

Environment :

  • BIO-REFINERY: Traditional raw materials based on petroleum carbon are replaced by materials based on renewable vegetal carbon or co-produced by other industrial processes.
  • RESIN FORMULATION: Green chemistry techniques ensure energy-efficient formulation and fewer harmful by-products.
  • SUPER SAP: technology that saves energy, minimises harmful by-products and reduces greenhouse gas emissions.

 

Application tips:

  • For best results, measure both components by weight to within 5% of the recommended mixing ratio.
  • Always mix the product for at least two minutes, scraping the container to ensure thorough mixing.
  • Use products in a controlled environment; avoid high humidity and low temperatures.
  • Animes, a by-product of the curing process, appear as a waxy film on the cured epoxy and are more visible in cool, damp conditions. It can clog the sandpaper and inhibit adhesion.
  • The amine is soluble in water and is easily removed with clean water (no solvent) and an abrasive pad.
  • For good adhesion, epoxy bonding surfaces must be clean, dry and sanded.
  • If you are unfamiliar with the product, create small test samples before starting a larger scale project.

 

Available options :

 

Resin ONE + fast hardener ONF

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:43

Mixing viscosity (cPs at 25°C): 1020

Time of use (at 25°C): 18 minutes

Dry to the touch (at 25°C): 3 hours

Recommended complete curing: 7 days at 25°C

Characteristics:slightly amber colour

Applications: general laminating work, gluing, coating, manual layering of layers

Resin ONE + slow hardener ONS

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:43

Mixing viscosity (cPs at 25°C): 1020

Time of use (at 25°C): 43 minutes

Dry to the touch (at 25°C): 8 hours

Recommended full cure: 7 days at 25°C (post cure recommended)

Characteristics: slightly amber colour

Applications: general laminating work, gluing, coating, manual layering of layers



Read more
Product Details
ER-ONE-2

Data sheet

ENTROPY
Biobased ( +/- 30%)
Choice of your ONE resin format
Resin ONE