Reference:
KIT-ONE-1.43F

KIT ONE 1.43F. ONE 1kg low viscosity bio-based laminating resin + ONF 0.43kg fast hardener

Biobased epoxy resin with high content of bio-components for lamination, composite applications, coating and adhesives

Fast curing, low viscosity and fast air release property.

Common uses: Fiberglass composites, natural fiber composites, woodworking, epoxy coatings, fiberglass boat repair, adhesives and sealants, surfboards, Stand Up Paddle Boards and Handplanes

Super Sap® formulation.

30% biobased content

USDA BioPreferred Certified

Read more
€75.90 (VAT incl.)
Description

ONE is a general purpose laminating resin with a high biobase content for laminating, coating and bonding applications of composites.

This system features faster speed, low viscosity, fast debubbling, ideal for fibre reinforced composite lamination and coating.

ONE is a USDA-certified BioPreferred® product with a 30% biobase content.

Usage: wood, coating, marine application, gluing

Consumption: a 6L kit = 32.5m². Consumption is reduced by 50% on porous substrates or fibre reinforcement.

Working temperature : optimal temperature from 21°C to 30°C.

Environment :

  • BIO-REFINERY: Traditional raw materials based on petroleum carbon are replaced by materials based on renewable vegetal carbon or co-produced by other industrial processes.
  • RESIN FORMULATION: Green chemistry techniques ensure energy-efficient formulation and fewer harmful by-products.
  • SUPER SAP: technology that saves energy, minimises harmful by-products and reduces greenhouse gas emissions.

 

Application tips:

  • For best results, measure both components by weight to within 5% of the recommended mixing ratio.
  • Always mix the product for at least two minutes, scraping the container to ensure thorough mixing.
  • Use products in a controlled environment; avoid high humidity and low temperatures.
  • Animes, a by-product of the curing process, appear as a waxy film on the cured epoxy and are more visible in cool, damp conditions. It can clog the sandpaper and inhibit adhesion.
  • The amine is soluble in water and is easily removed with clean water (no solvent) and an abrasive pad.
  • For good adhesion, epoxy bonding surfaces must be clean, dry and sanded.
  • If you are unfamiliar with the product, create small test samples before starting a larger scale project.

Available options :

 

Resin ONE + fast hardener ONF

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:43

Mixing viscosity (cPs at 25°C): 1020

Time of use (at 25°C): 18 minutes

Dry to the touch (at 25°C): 3 hours

Recommended complete curing: 7 days at 25°C

Characteristics:slightly amber colour

Applications: general laminating work, gluing, coating, manual layering of layers

 

Resin ONE + slow hardener ONS

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:43

Mixing viscosity (cPs at 25°C): 1020

Time of use (at 25°C): 43 minutes

Dry to the touch (at 25°C): 8 hours

Recommended full cure: 7 days at 25°C (post cure recommended)

Characteristics: slightly amber colour

Applications: general laminating work, gluing, coating, manual layering of layers

Read more
Product Details
KIT-ONE-1.43F

Data sheet

ENTROPY
Biobased ( +/- 30%)
Choice of your ONE resin format
Kit
Related products