Reference:
ER-305-IBC

ENTROPY 305 biobased resin. For high temperature compression molding processes (1000kg)

Biobased epoxy resin for compression molding processes for fast cycling

Rapid heat activated polymerization for high temperature compression molding processes.

Common uses: Skis and Snowboards, Skateboards, Compression molding composites, Wood laminates.

To be combined with CPS slow hardeners and CPF fast hardeners

Super Sap® formulation.

28% biobased content

USDA BioPreferred® certified

Read more
€10,991.04 (VAT incl.)
In stock 10 Items

   

Description

Resin 305 is a compression molding resin for rapid cycling in heat-assisted molding processes of fiber reinforced composites.

The 305 system has a high organic content, excellent fiber impregnation qualities and thixotropic characteristics to limit sagging in high temperature curing applications.

High modulus combined with excellent elongation properties results in durable yet lightweight composite parts.

305 epoxy resin is a USDA BioPreferred product with a 28% biobased content

Usage : skateboard, skis, snowboards, press molding composites

Consumption: about 3 liters for 2 snowboards or 2 pairs of skis

Usage advice:

-For best results, make the mixing ratio of the two components according to the weights

-Always mix the product thoroughly for at least 2 minutes, scraping all surfaces of the container to ensure even mixing

-Use the product in an environment with cold ambient temperatures or high humidity

-For optimum curing performance, make sure surfaces are dry and free of dirt, debris and/or oil. Surface preparation by sanding is strongly recommended

-Conduct pre-testing with the materials and processes being considered to fully understand the curing characteristics of the epoxy in your working environment with the materials.

 Available options:

 - 305 CPM resin + CPF fast curing agent

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:40

Mixing viscosity (cPs) at 25°C : 1994

Pot life at 25°C : 20 minutes

Recommended full cure: 15 minutes at 82°C

Characteristics : superior adhesion, very low viscosity to facilitate the wetting of the fibers and accelerate the polymerization for high production rates.

- 305 CPM resin + CPS fast hardener

Mixing ratio by volume: 2:1

Mixing ratio by weight: 100:38

Mixing viscosity (cPs) at 25°C : 1546

Pot life at 25°C: 50 minutes

Recommended full cure: 20 minutes at 82°C

Characteristics: Superior adhesion, very low viscosity to facilitate fiber wetting.





Read more
Product Details
ER-305-IBC

Data sheet

ENTROPY
Biobased ( +/- 30%)
Choice of your 305 resin format
Resin 305
Related products